1，本司出售的塑胶均可随货提供物性数据、SGS报告 、RoHS(环保)报告、MSDS(出厂证明)报告以及UL黄卡。FDA, LFGB报告,均可开17%增值税
TPE 6356 TPE6356 TPE 6356
| TPE 6356 美国杜邦公司 物性数据 |
| 暂无此原料描述部分┄ |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||
| 基本性能 | 24小时吸水率 | --- | ASTM D-570 | 0.3 | % | ||||||||
| 物理性能 | 泰伯磨耗量 | CS-17轮 | ASTM D-1044 | 7 | mg/1000rev | ||||||||
| 比重 | --- | ASTM D-792 | 1.22 | --- | |||||||||
| 熔体流动速率 | --- | ASTM D-1238 | 8.5 | g/10min | |||||||||
| 泰伯磨耗量 | H 18轮 | ASTM D-1044 | 77 | mg/1000rev | |||||||||
| 机械性能 | 硬度计硬度 | --- | ASTM D-2240 | 63 | --- | ||||||||
| 揉曲模量 | 23℃ | ASTM D-790 | 330 | Mpa | |||||||||
| 断裂拉伸力 | --- | ASTM D-638 | 41 | Mpa | |||||||||
| 断裂伸长 | --- | ASTM D-638 | 420 | % | |||||||||
|
--- |
|
|
|
|||||||||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 不破裂 | J/m | |||||||||
| 初耐撕裂性能 | --- | ASTM D-1004 | 175 | kn/m | |||||||||
| 热 性 能 | 熔点 | --- | ASTM D-3418 | 211 | ℃ | ||||||||
| 维卡软化点 | --- | ASTM D-1525 | 95 | ℃ | |||||||||
| 热畸变温度 | @0.5Mpa | ASTM D-648 | 115 | ℃ | |||||||||
| 热畸变温度 | @0.18Mpa | ASTM D-648 | 51 | ℃ | |||||||||
| 其它性能 | 耐揉曲切口增长性能 | --- | ASTM D-1052 | >5×105 | |||||||||
-
可用一般的热塑性塑料成型机加工，不需要特殊的加工设备。
2. 生产效率大幅提高。可直接用橡胶注塑机硫化，时间由原来的20min左右，缩短到1min以内；由于需要的硫化时间很短，因此已可用挤出机直接硫化，生产效率大幅提高。
3. 易于回收利用，降低成本。生产过程中产生的废料（逸出毛边、挤出废胶）和最终出现的废品，可以直接返回再利用；用过的TPE旧品可以简单再生之后回收利用，减少环境污染，扩大再生资源来源。
4. 节能。热塑性弹性体大多不需要硫化或硫化时间很短，可以有效节约能源。以高压软管生产能耗为例：橡胶为188MJ/kg，TPE为144MJ/kg，可节能达25%以上。
5. 应用领域更广。由于TPE兼具橡胶和塑料的优点，为橡胶工业开辟了新的应用领域。
6. 可用于塑料的增强、增韧改性。自补强性大，配方简化，配合剂对聚合物的影响制约小，质量性能更易掌握。但TPE的耐热性不如橡胶，随着温度上升而物性下降幅度较大，因而适用范围受到限制。同时，压缩变形、弹性回复、耐久性等同橡胶相比较差，价格上也往往高于同类橡胶。尽管如此，TPE的优点仍十分突出，各种新型的TPE产品也不断开发出来。作为一种节能环保的橡胶新型原料，发展前景十分看好。